Magnetically confined LIBS; Diatomic transition lines; TiO gamma;INDUCED BREAKDOWN SPECTROSCOPY; OPTICAL-EMISSION; LASER; ALLOYS; FIELD; ENHANCEMENT; NDYAG

This paper is focused on the clarification of the behaviour of various atomic, ionic, and TiO gamma (A(3)Phi-X-3 Delta, Delta v =0) diatomic transition lines as well as the continuum radiations in laser-induced titanium plasma plume by a pair of NdFeB. Depending on their different amount of impressionability from applied fields and electron-impact excitation rate, the responses of each component in optical emission spectrum and background continuum radiation to different applied magnetic field strengths (similar to 0.42-1.12 T) are significantly different. At magnetic fields of 0.98 and 1.12 T, the amount of impressionability for Ti i: 388.2 nm is higher than others, while for TiO gamma molecular transitions, the amount of impressionability factor in a 0.98 T field strength is considerable, because in the first moments after the laser pulse the continuum radiation is dominant, by applying an external magnetic field, this amount of radiation be reduced. The temporal evolution of the optical emission lines shows that choosing a suitable time delay and gate width has a considerable role in further impressionability of externally applied field in case of different elements. The electron density Ne varied from 0.99x10(17) to 11.53x10(17) cm(-3), and the plasma temperature T-e, was obtained in a range of 4835-16818 K by employing maximum applied field of 1.12 T. The supplementary investigations will be conducted towards further improvements of the purposeful analysis of each component in confined plasma by magneto-LIBS technique in order to find new approaches in the field of magnetic confinement.

Laser-induced Breakdown Spectroscopy; Atomic Spectroscopy; Molecular Spectroscopy; Laser Ablation; 'lime-resolved Spectroscopy; Spectroscopy in Chemical Analysis;INDUCED BREAKDOWN SPECTROSCOPY; LINES; DENSITY; SPECTRA

This article gives a brief review of experimental studies of hydrogen Balmer series emission spectra. Ongoing research aims to evaluate early plasma evolution following optical breakdown in laboratory air. Of interest is as well laser ablation of metallic titanium and characterization of plasma evolution, Emission of titanium monoxide is discussed together with modeling of diatomic spectra to infer temperature. The behavior of titanium particles in plasma draws research interests ranging from the modeling of stellar atmospheres to the enhancement of thin film production via pulsed laser deposition,

IN-SITU ANALYSIS; ABLATION; REMOVAL; METAL; NANOSECOND; COATINGS; STEEL; MELTS

Titanium metal injection molding allows creation of complex metal parts that are lightweight and biocompatible with reduced cost in comparison with machining titanium. Laser-induced breakdown spectroscopy (LIBS) can be used to create plasma on the surface of a sample to analyze its elemental composition. Repetitive ablation on the same site has been shown to create differences from the original sample. This study investigates the potential of LIBS for selective surface sintering of injection-molded titanium metal. The temperature created throughout the LIBS process on the surface of the injection-molded titanium is high enough to fuse together the titanium particles. Using the ratio of the Ti II 282.81 nm and the C I 247.86 nm lines, the effectiveness of repetitive plasma formation to produce sintering can be monitored during the process. Energy-dispersive X-ray spectroscopy on the ablation craters confirms sintering through the reduction in carbon from 20.29 Wt.% to 2.13 Wt.%. Scanning electron microscope images confirm sintering. A conventional LIBS system, with a fixed distance, investigated laser parameters on injection-molded and injection-sintered titanium. To prove the feasibility of using this technique on a production line, a second LIBS system, with an autofocus and 3-axis translation stage, successfully sintered a sample with a nonplanar surface.

PLASMA-MASS SPECTROMETRY; VACUUM-ULTRAVIOLET; ABLATION; STEEL; COAL

The laser-induced breakdown spectroscopy (LIBS) with a frequency quintupled 213 nmNd:YAG laser was examined to the analysis of trace level of carbon (C) in high-purity metals and its detection and analytical capabilities were evaluated. Though C signal in a wavelength of 247.9 nm, which showed the highest sensitivity of C, could be obtained from Cd, Ti, and Zn ca. 7000 mg kg(-1) C in Fe could not be detected due to the interferences from a lot of Fe spectra. Alternative C signal in a wavelength of 193.1 nm could not be also detected from Fe due to the insufficient laser output energy of the frequency quintupled 213 nm Nd:YAG laser. The depth analysis of C by LIBS was also demonstrated and the C in Cd and Zn was found to be contaminated in only surface area whereas the C in Ti was distributed in bulk. From these results, the frequency quintupled 213 nm Nd:YAG laser, which was adopted widely as a commercial laser ablation (LA) system coupled with inductively coupled plasma mass spectrometry (ICPMS) for trace element analysis in solid materials, could be used for C analysis to achieve simultaneous measurements for both C and trace elements in metals by LIBS and LA-ICPMS, respectively.