INDUCED BREAKDOWN SPECTROSCOPY; EMISSION-SPECTROSCOPY; ABLATION; ENHANCEMENT; TITANIUM; ALUMINUM; METALS

The role of spatial confinement for improvement of laser-induced Mg plasma parameters and growth of surface features is investigated by introducing a metallic blocker. Nd: YAG laser at various fluences ranging from 7 to 28 J cm(-2) was employed as an irradiation source. All measurements were performed in the presence of Ar under different pressures. Confinement effects offered by metallic blocker are investigated by placing the blocker at different distances of 6, 8 and 10 mm from the target surface. It is revealed from laser-induced breakdown spectroscopy analysis that both plasma parameters, i.e., excitation temperature and electron number density initially increase with increasing laser fluence due to enhancement in energy deposition. With further increase in laser fluence, a decreasing trend followed by saturation is observed which is attributable to shielding effect and self-regulating regime. It is also observed that spatial confinement offered by metallic blocker is responsible for the significant enhancement of both electron temperature and electron number density of Mg plasma. This is true for all laser fluences and pressures of Ar. Maximum values of electron temperature and electron number density without blocker are 8335 K and 2.4 x 10(16) cm(-3), respectively, whereas these values are enhanced to 12,200 K and 4 x 10(16) cm(-3) in the presence of the blocker. The physical mechanisms responsible for the enhancement of Mg plasma parameters are plasma compression, confinement and pronounced collisional excitations due to reflection of shock waves. Scanning electron microscope analysis was performed to explore the surface morphology of laser-ablated Mg. It reveals the formation of cones, cavities and ripples. These features become more distinct and well defined in the presence of the blocker due to plasma confinement. The optimum combination of blocker distance, fluence and Ar pressure can identify the suitable conditions for defining the role of plasma parameters for surface structuring.

Electron number density; Electron temperature; Laser-induced breakdown spectroscopy; Spatial confinement; Spectral emissions;PLASMA; TEMPERATURE; ABLATION; DENSITY

Spatial confinement effects on plasma parameters and surface morphology of laser-ablated Mg are studied by introducing a metallic blocker as well as argon (Ar) gas at different pressures. Nd: YAG laser at various fluences ranging from 7 to 28 J/cm(2) was employed to generate Mg plasma. Confinement effects offered by metallic blocker are investigated by placing the blocker at different distances of 6, 8, and 10 mm from the target surface; whereas spatial confinement offered by environmental gas is explored under four different pressures of 5, 10, 20, and 50 Torr. Laser-induced breakdown spectroscopy analysis revealed that both plasma parameters, that is, excitation temperature and electron number density initially are strongly dependent upon both pressures of environmental gases and distances of blockers. The maximum electron temperature of Mg plasma is achieved at Ar gas pressure of 20 Torr, whereas maximum electron number density is achieved at 50 Torr. It is also observed that spatial confinement offered by metallic blocker is responsible for the significant enhancement of both electron temperature and electron number density of Mg plasma. Maximum values of electron temperature and electron number density without blocker are 8335 K and 2.4 x 10(16) cm(-3), respectively, whereas these values are enhanced to 12,200 K and 4 x 10(16) cm(-3) in the presence of blocker. Physical mechanisms responsible for the enhancement of Mg plasma parameters are plasma compression, confinement and pronounced collisional excitations due to reflection of shock waves. Scanning electron microscope analysis was performed to explore the surface morphology of laser-ablated Mg. It reveals the formation of ripples and channels that become more distinct in the presence of blocker due to plasma confinement. The optimum combination of blocker distance, fluence and Ar pressure can identify the suitable conditions for defining the role of plasma parameters for surface structuring.

INDUCED BREAKDOWN SPECTROSCOPY; LIBS; SAMPLES

In this study, Nd: YAG laser pulse is used to ablate the Magnesium sample for laser induced breakdown spectroscopy analysis. The emission lines are plotted for ionic and atomic element of Mg I and Mg II respectively. The emission lines of Mg I and Mg II were recorded at wavelength of 279.55 nm, 280.27 nm and 285.21 nm. The analysis including the different of gate delay, determination of signal to background ratio and calibration curve of different concentration of magnesium is discussed in details.